Current location:Home >  Products  >  Epoxy curing agent series
Products/
JHL-2012 New stone compound rubber
      DetailsMore
      JHL-2012 New stone compound rubber

      JHL-2012 is a silicone-based epoxy resin stone compound adhesive designed for bonding or mutual adhesion of marble, granite, ceramic tile, Aite board, insulation board, cement foam board, PPC board and so on. Is a wet surface curing adhesive. Can also be used for mortar concrete interface re-construction joints.

      Product Features:

      ◆ low viscosity, easy operation, the amount of glue per unit area less.

      ◆ has excellent resistance to freeze-thaw performance.

      ◆ With the impact of lower ambient temperature, low temperature can also be construction, 25 hours, 2 hours can be dismantled frame, 4 hours basic curing, 6 hours to enter the next process.

      ◆ Low surface treatment of the substrate surface also has good adhesion, with water in the surface can also be a good bonding effect.

      ◆ has excellent water resistance, corrosion resistance.

      ◆ AB group distribution ratio of 1: 1, the ratio of deployment is not easy to error, particularly suitable for short construction cycle of the composite operation.


      The main technical and performance parameters:

      project   

      Typical values

      Exterior   

      A

      Beige to light gray viscous liquid

      B

      Beige to khaki viscous liquid

      Viscosity  

      A

      15000~25000

      B

      15000~25000

      Mixing ratio A: B 

      11

      100 g cup gel time

      20min~30min

      25 ℃ curing time table dry / hard work  

      2h/6h

      Solid content

      ≥95


      Product use method:

      ◆ open the AB plastic drums, should be first with a special stirrer will A agent, B agent were stirring (A, B stirrer can not be mixed, otherwise the glue is easy to respond to agglomeration resulting in hollowing), to avoid long-term storage lead to a small amount of layered adhesive Results.

      ◆ The sizing surface should be kept dry, there is no obvious water stains, dust and oil, pay special attention to the water inside the cave to be clean, should try to be dried and sticky objects to keep the sticky surface above 25 ℃.

      ◆ A component and B component according to A: B = 1: 1 deployment is used to cash in 10 ~ 15 min to complete.

      ◆ glue, such as touch dry after stacking. Polishing, to be such a layer of hard work.


      Product use Note:

      ◆ This series of special glue, applies only to stone and stone, ceramic tile and other non-metallic substrate composite, the applicable period (operating time) affected by temperature, high temperature is applicable to short.

      ◆ Sizing should be completely according to the ratio of A: B = 1: 1 deployment to ensure the best bonding effect, otherwise it will affect the bonding strength.

      ◆ A, B glue should be fully mixed after mixing, the product after curing the surface shiny, such as glue layer after curing the surface of filamentous or massive color, indicating A, B plastic mixing is not sufficient.

      ◆ AB plastic drums open, you should first use a special stirrer will A agent, B agent were stirring. If not stirred evenly, may lead to pink water stains on the board surface, the plastic layer of soft and degumming phenomena.

      ◆ JHL-2012 is a wet surface curing adhesive, adhesives, low molecular weight substances are also soluble in water. For the high iron content of the plate, such as: sago, old rice, wood fossils and other light-colored sheet metal such as Ascot white. Requirements of double-sided adhesive coating plate to reduce the hollowing, to avoid the concentration of water vapor spill stone surface. Resulting in a pink watermark. This kind of plate composite interface shall not have obvious water stains. Production may be appropriate to reduce the amount of curing agent (down to 90%), the appropriate extension to the next process of production time.

      ◆ time should not be too much time to adjust the plastic, glue the number of more likely to be due to fast response and slightly shortened the pot life. To 25 ℃ when used within 15 minutes is appropriate, the deployment of a good plastic should be used once

      ◆ The workshop should be well ventilated. This product may stimulate the skin of some people, when the glue should do a good job of labor protection, glue splashed on the skin should be immediately rubbed with acetone or advanced hand sanitizer, then rinse with water, when splashed into the eyes, the application of large amounts of water Rinse and seek immediate medical attention.

      ◆ Although this product can be composite panel and substrate in the case of high temperature as usual compound, but should still try to keep the adhesive surface dry, such as dry lines have been built, can still be short-term drying, and other stone and Substrate surface drying and then compound, will be able to get a better bonding effect.

      ◆ When the ambient temperature is too low, the glue will thicken and slow down the curing speed, can be heated by A glue on the stone to warm or improve the temperature of the construction environment to make glue thinning, and thus speed up the curing speed. It is worth noting that: The ideal curing temperature of the composite rubber is 25 ℃ ~ 75 ℃; when the temperature is too low in winter, as far as possible heating curing (such as a drying line has been built for a short time baking, or gas gun And so on the stone surface for a short time baking), will be able to get a better curing effect, otherwise there may be a low intensity of the situation.

      ◆ The components of the product should be sealed and stored in a cool warehouse, to avoid direct sunlight, the opening of the A plastic and B plastic Do not cover the wrong lid.


      Packaging, transportation and storage:

      1, packaging 25KG iron or plastic packaging specifications.

      2, the transport process should be rain, sun, to prevent damage to the packaging, moisture.

      3, stored in a cool dry place, away from fire, strong acid, alkali and strong oxidants.

      4, in accordance with the provisions of the transport and storage conditions, from the date of production from the storage period of 12 months.

      5, JHL-2012 for non-dangerous goods, according to the general merchandise disposal.

      6, the color is gradually deepening during storage is a normal phenomenon, does not affect the use of results. After opening the use of packaging barrels should be tightly closed lid, to avoid long-term exposure to air.


      Special Note:

      The Company of the above data and text description are from sincerity, but I do not know whether it is suitable for your company's construction technology and use. Therefore, please use this product before the samples from the Company to obtain the test, if you have any questions, please feel free to contact the Company.